Konpozisyon chimik
| Konpozisyon chimik | ||||
| API 5L X42 PSL1 (San pwoblèm) |
API 5L X42R PSL2 (San pwoblèm ak soude) |
API 5L X42N PSL2 (San pwoblèm ak soude) |
API 5L X42Q PSL2 (San pwoblèm ak soude) |
|
| Kabòn (C) max | 0.28% | 0.24% | 0.24% | 0.180% |
| (Si) max | - | 0.40% | 0.40% | 0.450% |
| Manganèz (Mn) max | 1.30% | 1.20% | 1.20% | 1.400% |
| Fosfò (P) max | 0.03% | 0.03% | 0.03% | 0.025% |
| Souf (S) max | 0.03% | 0.02% | 0.02% | 0.015% |
| Vanadyòm (V) | - | 0.06% | 0.06% | 0.050% |
| Niobyòm (Nb) | - | 0.05% | 0.05% | 0.050% |
| Titàn (Ti) | - | 0.04% | 0.04% | 0.040% |
| Vanadyòm (V) + Niobyòm (Nb) + Titàn (Ti) | 0.15% | - | - | - |
| Cu Mwens pase oswa egal a {{0}}.5%,Ni Mwens pase oswa egal a 0.3%,Cr Mwens pase oswa egal a 0.3%,Mo Mwens pase oswa egal a 0.15% | ||||
| Konpozisyon chimik | ||
| Mwens pase oswa egal a 25mm soude | API 5L X42 PSL1 | API 5L X42M PSL2 |
| Kabòn (C) max | 0.26% | 0.220% |
| (Si) max | - | 0.450% |
| Manganèz (Mn) max | 1.30% | 1.300% |
| Fosfò (P) max | 0.03% | 0.025% |
| Souf (S) max | 0.03% | 0.015% |
| Vanadyòm (V) | - | 0.050% |
| Niobyòm (Nb) | - | 0.050% |
| Titàn (Ti) | - | 0.040% |
| Vanadyòm (V) + Niobyòm (Nb) + Titàn (Ti) | 0.15% | - |
| Cu Mwens pase oswa egal a {{0}}.5%,Ni Mwens pase oswa egal a 0.3%,Cr Mwens pase oswa egal a 0.3%,Mo Mwens pase oswa egal a 0.15% | ||
- PSL1: Pou Klas X2, maksimòm lankontni kabònse tipikmanpi wonan PSL1 konpare ak PSL2. Fosfò ak souf kontni tou gen pi wo limit maksimòm nan tiyo PSL1.
- PSL2: PSL2 gen pi ba limit maksimòm pou kabòn, fosfò, ak souf, ki kontribye nanpi bon soudabilite ak fòmabilite. Anplis de sa, PSL2 limite kontni ekivalan kabòn, ki enpòtan anpil pou kontwole dite ak soudabilite asye a.
Pwopriyete mekanik
| Pwopriyete Fizik | ||
| API 5L X42 PSL1 | API 5L X42(R,N,Q,M) PSL2 | |
| sede fòs | Pi gran pase oswa egal a 290MPa (42100psi) | 290MPa(42100psi) - 495MPa(71800psi) |
| fòs rupture | Pi gran pase oswa egal a 415MPa (60200psi) | Pi gran pase oswa egal a 415MPa(60200psi) - 760Mpa(110200psi) |
| elongasyon (50mm 2 pous) | 21.00% | 28.00% |
- PSL1: Sede minimòm ak fòs rupture pou Klas X2 nan PSL1 satisfè kondisyon debaz yo, ak kontwòl mwens sevè sou valè maksimòm yo.
- PSL2: PSL2 tiyo gen yon limit sou maksimòm sede a ak fòs rupture, asire pwopriyete mekanik ki pi konsistan. Severite frakti se tou yon kondisyon obligatwa pou tiyo PSL2, ki pa obligatwa pou PSL1.
Aplikasyon
- PSL1: Apwopriye pousèvis jeneralaplikasyon kote demand yo sou pwopriyete mekanik tiyo a ak konpozisyon chimik yo pa tankou kritik.
- PSL2: Ideyal pou plisaplikasyon pou mande, tankougwo presyonoswakoroziviteanviwònman, kote pwopriyete mekanik siperyè ak pite chimik yo obligatwa, tankou tiyo transmisyon segondè presyon, enstalasyon lanmè, ak tiyo anba lanmè.
Avantaj
- PSL1: Ofri yonbalans pri ak pèfòmans, fè li apwopriye pou aplikasyon pou mwens kritik kote espesifikasyon ki pi wo nan PSL2 yo pa nesesè.
- PSL2: lapi sevèkontwòl sou pwopriyete mekanik, pi sere kontwòl konpozisyon chimik, ak plis rijidtès ki pa destriktif (NDT)kondisyon. Tiyo PSL2 sibi NDT plis konplè, asire entegrite sistèm tiyo a epi minimize risk pou echèk oswa fwit pandan operasyon an. Laestanda pi sevènan PSL2 tou kontribye nan amelyore sekirite ak fyab nan kondisyon sèvis grav.
An rezime, chwa ki genyen ant API 5L PSL1 ak PSL2 pou tiyo asye Klas X2 depann de kondisyon espesifik aplikasyon yo.PSL1 adekwat pou aplikasyon estanda, pandanPSL2 rezève pou anviwònman ki pi difisilki mande pèfòmans siperyè tiyo ak bon jan kalite. Chwa ant PSL1 ak PSL2 ta dwe baze sou kondisyon espesifik pwojè a,ak PSL2 se chwa ki pi pito pou aplikasyon pou mande pèfòmans siperyè tiyo ak asirans kalite.